Both of the standards cover 8 grades of titanium & titanium alloys: titanium Grade 1 (Ti 1,R50250), Grade 2 (Ti 2, R50400), Grade 4 (Ti 4,R50700), Grade 5 (Ti 5,R56400), Grade 7 (Ti 7,R52400), Grade 19 (Ti 19,R58640, Ti-38-6-44), Grade 23 (Ti 23,R56401, Ti-6Al-4V ELI), Grade 32 (Ti 32,R55111, Ti-5-1-1-1). The fasteners can be cold formed, hot formed, or machined from suitable material.
Titanium Ti Grade 2 hex head bolts, Titanium alloy Machinning products manufacturer
3.7035 Hex bolt | TI2 Hex bolt manufacturer
We have stock of nut and washer of Ti2,Ti5,Ti7
Artisan Industry, Specilize in Titanium fasteners!
Competitive titanium price per kg 2021!
Experienced worker!
Professional sales!
Short delivery time!
Titanium alloy products, ti6al4v bolts,nuts.U bolts,threaded rods,washers,flange according to standard or drawing.
1. Standard:DIN931/933,ISO4014/4017,ASME B 18.2.1
2. Material: 316 Ti; 3.7035/Ti Gr-2; 3.7235/Ti Gr-7;Ti Gr-5
3. Size: M3-24
4. Delivery time: 35 days
5. Packing: Bulk in 25kgs ctn
Titanium & Titanium Alloy Bolts and Nuts Chemical Composition:
Grade 1(Ti1, R50250), w.t %: C≤0.10, Fe≤0.20, Ti: balance, H≤0.0125, N≤0.05, O≤0.18, Residuals: each≤0.10, total≤0.40.
Grade 2(Ti2, R50400), w.t %: C≤0.10, Fe≤0.30, Ti: balance, H≤0.0125, N≤0.05, O≤0.25, Residuals: each≤0.10, total≤0.40.
Grade 4(Ti4, R50700), w.t %: C≤0.10, Fe≤0.50, Ti: balance, H≤0.0125, N≤0.07, O≤0.40, Residuals: each≤0.10, total≤0.40.
Grade 5(Ti5,R56400) Titanium Ti-6Al-4V (Grade 5), w.t %: Al:5.5~6.75, C≤0.10, Fe≤0.40, Ti: balance, H≤0.0125, N≤0.05, O≤0.20, V:3.5~4.5, Residuals: each≤0.10, total≤0.40.
Grade 7(Ti7,R52400), w.t %: C≤0.10, Fe≤0.30, Ti: balance, H≤0.0125, N≤0.05, O≤0.25, Pd:0.12~0.25, Residuals: each≤0.10, total≤0.40.
Grade 19(Ti19,R58640), w.t %: Al:3.0~4.0, C≤0.05, Fe≤0.30, Ti: balance, H≤0.0200, N≤0.03, O≤0.12, Pd≤0.10, V:7.5~8.5, Cr:5.5~6.5, Mo:3.5~4.5, Zr:3.5~4.5, Ru:≤0.10, Residuals: each≤0.15, total≤0.40.
Grade 23(Ti23,R56401), w.t %: Al:5.5~6.5, C≤0.08, Fe≤0.25, Ti: balance, H≤0.0125, N≤0.05, O≤0.13, V:3.5~4.5, Residuals: each≤0.10, total≤0.40.
Grade 32(Ti32,R55111) w.t %: Al:4.5~5.5, C≤0.08, Fe≤0.25, Ti: balance, H≤0.0125, N≤0.03, O≤0.11, V:0.6~1.4, Mo:0.6~1.2, Zr:0.6~1.4, Sn:0.6~1.4, Si:0.06~1.4, Residuals: each≤0.15, total≤0.40.
ASTM F468 / F468M Titanium & Titanium Alloy Bolts, Screws & Studs
Titanium and Titanium Alloy | Tensile Strength, min. | Yield Strength, min. | Hardness | Elongation | ||
Ti Grade | ksi | MPa | ksi | MPa | - | min. % |
Ti 1 | 35 | 240 | 25 | 170 | 140~160 HV | 24 |
Ti 2 | 50 | 345 | 40 | 275 | 160–180 HV | 20 |
Ti 4 | 80 | 550 | 70 | 483 | 200–220 HV | 15 |
Ti 5*Class A | 130 | 895 | 120 | 828 | 30–39 HRC | 10 |
Ti 5*Class B | 130 | 895 | 120 | 828 | 30–39 HRC | 10 |
Ti 7 | 50 | 345 | 40 | 275 | 160–180 HV | 20 |
Ti 19 | 120 | 793 | 115 | 759 | 24–38 HRC | 15 |
Ti 23 | 120 | 828 | 110 | 759 | 25–36 HRC | 10 |
Ti 32 | 100 | 690 | 85 | 585 | 24–38 HRC | 10 |
Titanium and Titanium Alloy | Hardness | Proof Stress | |
Ti Grade | min. | ksi | MPa |
Ti 1 grade 1 titanium | 140 HV | 40 | 275 |
Ti 2 grade 2 titanium | 150 HV | 55 | 380 |
Ti 4 grade 4 titanium | 200 HV | 85 | 585 |
Ti 5 grade 5 titanium | 30 HRC | 135 | 930 |
Ti 7 grade 7 titanium | 160 HV | 55 | 380 |
Ti 19 grade 19 titanium | 24 HRC | 120 | 825 |
Ti 23 grade 23 titanium | 25 HRC | 125 | 860 |
Ti 32 grade 32 titanium | 24 HRC | 105 | 725 |